Austmig ESD2
Solid MIG Wire
The Austmig ESD2 is a copper coated, all positional low alloy MIG wire used for welding medium to high strength steels, particularly where service temperatures up to 500° C are encountered. It gives excellent resistance to porosity using Argon based gas mixtures (i.e. Ar/CO², Ar/O², Ar/CO²/O²).
AS/NZS 14341-B-G 57A 5U M21 S4M31
AWS A5.28 ER80S-D2
AWS A5.28 ER90S-D2
Applications
TUBULAR SECTIONS
TRAILERS
STRUCTURAL WELDING
STORAGE TANKS
SHEET PLATE & STEEL GALVANISED OR OTHERWISE
HOOPERS
DUCT WORK
Excellent Resistance to Porosity
Austmig ESD2 provides a consistently sound weld deposit even when porosity is a potential problem due to dirty or rusty surfaces.
Specifications
Typical All Weld Metal Chemical Analysis
C
0.85
Mn
1.825
Si
0.70
Cu
0.30
Mo
0.50
Ni
0.10
Cr
0.15
Typical All Weld Metal Mechanical Analysis
Gas Type
Ar+18% CO²
CO²
Yield Stress
680 MPa
631 MPa
Tensile Strength
712 MPa
694 MPa
Elongation
27%
24%
CVN Impact Values
110J @ -50ºC
35J @ -50ºC
Resources
Austmig ESD2
Solid MIG Wire
The Austmig ESD2 is a copper coated, all positional low alloy MIG wire used for welding medium to high strength steels, particularly where service temperatures up to 500° C are encountered. It gives excellent resistance to porosity using Argon based gas mixtures (i.e. Ar/CO², Ar/O², Ar/CO²/O²).
AS/NZS 14341-B-G 57A 5U M21 S4M31
AWS A5.28 ER80S-D2
AWS A5.28 ER90S-D2
Applications
HOPPERS
TRAILERS
DUCT WORK
STORAGE TANKS
TUBULAR SECTIONS
SHEET PLATE & STEEL GALVANISED OR OTHERWISE
STRUCTURAL WELDING
Specifications
Typical All Weld Metal Chemical Analysis
C
0.85
Mn
1.825
Si
0.70
Cu
0.30
Mo
0.50
Ni
0.10
Cr
0.15
Typical All Weld Metal Mechanical Analysis
Gas Type
Ar+18% CO²
CO²
Yield Stress
680 MPa
631 MPa
Tensile Strength
712 MPa
694 MPa
Elongation
27%
24%
CVN Impact Values
110J @ -50ºC
35J @ -50ºC