Vertiwear 600
Gas Shielded Hard Surfacing Flux Core MIG Wire
The Vertiwear 600 is an all position, hard surfacing flux cored wire depositing a multi-purpose martensitic steel alloy. It can be used to hard surface mild and low alloy steel components subject to moderate abrasion coupled with medium to high impact.
It also exhibits excellent compressive strength and metal to metal wear resistance. Excellent operator appeal in all positions.
Applications
DRAGLINE CHAINS
DOZER BLADES
RIPPER TEETH
FACING OF AGRICULTURAL POINTS & EQUIPMENT
SLIDING METAL PARTS
KILN TRUNNIONS
Superior Weld Metal Control
The Vertiwear 600 provides higher deposition rates and greater productivity in out of position applications.
Excellent Operator Appeal
The Vertiwear 600 exhibits excellent compressive strength and metal to metal wear resistance and provides excellent operator appeal in all postions.
Specifications
Typical All Weld Metal Chemical Analysis
C
0.40
Mn
0.75
Si
0.60
Cr
6.50
Mo
1.00
Fe
Bal
Typical All Weld Metal Mechanical Analysis
Hardness - Number Of Layers: 1
As-Deposited On 1020 Steel: 52 HRC
Hardness - Number Of Layers: 2
As-Deposited On 1020 Steel: 56 HRC
Hardness - Number Of Layers: 3-8
As-Deposited On 1020 Steel: 57 HRC
Hardness As-Deposited: 55 - Time At Temp: 10 Hours
Hardness After Tempting: 535°C: 54 HRc, 620°C: 46 HRc
Hardness As-Deposited: 55 - Time At Temp: 20 Hours
Hardness After Tempting: 535°C: 49 HRc, 620°C: 40 HRc
Hardness As-Deposited: 55 - Time At Temp: 80 Hours
Hardness After Tempting: 535°C: 47 HRc, 620°C: 40 HRc
Notes
Magnetic
Resources
Vertiwear 600
Gas Shielded Hard Surfacing Flux Core MIG Wire
The Vertiwear 600 is an all position, hard surfacing flux cored wire depositing a multi-purpose martensitic steel alloy. It can be used to hard surface mild and low alloy steel components subject to moderate abrasion coupled with medium to high impact.
It also exhibits excellent compressive strength and metal to metal wear resistance. Excellent operator appeal in all positions.
Applications
DRAGLINE CHAINS
DOZER BLADES
RIPPER TEETH
SLIDING METAL PARTS
FACING OF AGRICULTURAL POINTS & EQUIPMENT
KILN TRUNNIONS
Specifications
Typical All Weld Metal Chemical Analysis
C
0.40
Mn
0.75
Si
0.60
Cr
6.50
Mo
1.00
Fe
Bal
Typical All Weld Metal Mechanical Analysis
Hardness - Number Of Layers: 1
As-Deposited On 1020 Steel: 52 HRC
Hardness - Number Of Layers: 2
As-Deposited On 1020 Steel: 56 HRC
Hardness - Number Of Layers: 3-8
As-Deposited On 1020 Steel: 57 HRC
Hardness As-Deposited: 55 - Time At Temp: 10 Hours
Hardness After Tempting: 535°C: 54 HRc, 620°C: 46 HRc
Hardness As-Deposited: 55 - Time At Temp: 20 Hours
Hardness After Tempting: 535°C: 49 HRc, 620°C: 40 HRc
Hardness As-Deposited: 55 - Time At Temp: 80 Hours
Hardness After Tempting: 535°C: 47 HRc, 620°C: 40 HRc
Notes
Magnetic